This site is dedicated to topics of interest to our members, their employees, and other interested parties. We encourage our readers to submit any questions or points of view that may be of interest to others. Answers have been prepared and submitted by CCTIA members and are the opinion of the author. The answers do not represent an official position of CCTIA. For comments or questions, please contact us.

10.057 Water/Cement Ratio vs Strength
Q	Many published articles relate how changing the water-cement ratio has a large effect on concrete strength. Is there a simple explanation for this effect? -- Technician in San Leandro, California
A	2/09 - Response prepared by Terry Egland, a principle at Testing Engineers, Inc., and a registered engineer in California. In general, there exists a fundamental inverse relationship between porosity and strength of solids. This strength-porosity relationship is applicable to a wide range of materials, such as iron, stainless steel and granite. Think of examining a concrete core, which exhibits voids created by a lack of consolidation. You can imagine, why with a lack of internal structure, the compressive strength would be lower than expected. On a much smaller scale, there is a theoretical volume of water (based on curing conditions) required to hydrate a given volume of cement. Once you have added more than that amount, it creates
	capillary porosity (i.e. microscopic cavities or voids). The higher the water-cement ratio, the more porous and the weaker the strength. Generally, to maximize strength and durability, the water-cement ratio should be the lowest possible to hydrate the cement while maintaining its workability